Polyamide 6 injection molding grade, 25% glass fiber reinforced, flame retarded based on halogens
| Original Document | Technical Datasheet(German) | |||
| Features | Flame RetardantHalogenatedFilled & Reinforced | |||
| Additive | Flame Retardant | |||
| Processing | Injection | |||
| Reinforced | 25% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | Dry |
Water Absorption | *** % | ISO 62 | 23°C, Saturation |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C, 50% r.h. |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | Cond. |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | Dry, 23°C, 1 mm/Min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | Cond. |
Break | *** Mpa | ISO 527-1/-2 | Dry, 23°C, 5mm/Min |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | Cond. |
Break | *** % | ISO 527-1/-2 | Dry, 23°C, 5mm/Min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Melt Temperature(Tm) | *** °C | ISO 3146 | 10 K/min |
Continuous Use Temperature | |||
20000 hr | *** °C | IEC 60216 | |
Long term | *** °C | IEC 60216 | some hours |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
0.8mm | *** °C | IEC 60695-2-12 | |
1.6mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
0.8mm | *** °C | IEC 60695-2-13 | |
1.6mm | *** °C | IEC 60695-2-13 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 62631-3-1 | Cond. |
Volume Resistivity | *** Ohm-cm | IEC 62631-3-1 | Dry |
Surface Resistivity | *** Ohm | IEC 62631-3-2 | Cond. |
Surface Resistivity | *** Ohm | IEC 62631-3-2 | Dry |
Dielectric Constant(Permittivity) | |||
1MHz | *** - | IEC 62631-2-1 | Cond. |
1MHz | *** - | IEC 62631-2-1 | Dry |
Dissipation Factor | |||
1MHz | *** E-4 | IEC 62631-2-1 | Cond. |
1MHz | *** E-4 | IEC 62631-2-1 | Dry |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 | Dry |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.