Polypropylene copolymer compound obtained by industrial scraps, filled with 10% talc, UV stabilized, low odor and scratch resistant.
Flowability for injection molding, available in black version ( standard black and NOIR TITANE 205.375 ) and coloured as per sample.
| Original Document | Technical Datasheet(English) | |||
| Features | Anti-ScratchLow OdorUV StabiltiyCopolymerFilled & ReinforcedRecycled Contained | |||
| Additive | UV-Stabilizer | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Reinforced | 10% Talc | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Filled/Ash | *** % | ISO 3451 | |
Post Consumer Recycled | *** % | Internal | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flexural Modulus | *** Mpa | ISO 178 | 23°C, 2.0 mm/min |
Flexural Strength | |||
Yield | *** Mpa | ISO 178 | 23°C, 2.0 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1fA | |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/Bf | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/Af | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.