Homopolymer polypropylene compound 30 % filled with calcium carbonate.
Flowability for injection molding.
Available in natural versions and colored as per sample.
| Original Document | Technical Datasheet(English) | |||
| Features | Anti-StaticGood FlowHomopolymerFilled & Reinforced | |||
| Appearance | Pellets/GranulesNatural ColorBlack | |||
| Processing | Injection | |||
| Reinforced | 30% Calcium Carbonate | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/1 | 23°C |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2/50 | 23°C |
Break | *** Mpa | ISO 527-2/50 | 23°C |
Tensile Elongation | |||
Yield | *** % | ISO 527-2/50 | 23°C |
Break | *** % | ISO 527-2/50 | 23°C |
Flexural Modulus | *** Mpa | ISO 178 | 23°C, 2.0 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 23°C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-20℃ (-4℉) | *** kJ/m² | ISO 180/1A | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/Bf | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/Af | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A50 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.