Polypropylene homopolymer obtained by industrial scraps. 10% reinforced with glass fiber chemically coupled and 20% cellulose fiber.
Flowability for injection moulding.
Available in black version and colored as per sample.
| Original Document | Technical Datasheet(English) | |||
| Features | HomopolymerFilled & ReinforcedRecycled Contained | |||
| Appearance | Pellets/GranulesBlackGreen | |||
| Processing | Injection | |||
| Reinforced | 10% Glass Fiber20% Cellulose | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
Water Absorption | *** % | ISO 62 | 24 hr, 23°C |
Post Consumer Recycled | *** % | Internal | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/1 | 23°C |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2/50 | 23°C |
Tensile Elongation | |||
Break | *** % | ISO 527-2/50 | 23°C |
Flexural Modulus | *** Mpa | ISO 178 | 23°C, 2.0 mm/min |
Flexural Strength | |||
Yield | *** Mpa | ISO 178 | 23°C, 2.0 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.