PLEXIGLAS® Hi-Gloss NTA-5 black 9V022 is an amorphous thermoplastic molding compound, based on impact-modified polymethyl methacrylate (PMMA).
PLEXIGLAS® molding compounds have the following typical properties:
• high weather resistance
• brilliant appearance
• 100 % recyclable
PLEXIGLAS® Hi-Gloss NTA-5 black 9V022 is characterized by the following additional properties:
• highest breaking strength and impact resistance
• increased heat resistance
• improved resistance to stress cracking
• balanced property profile
Application:
PLEXIGLAS® Hi-Gloss NTA-5 black 9V022 is particularly suitable for injection molding of technical components where high impact resistance is needed. Due to its superior brilliance high-gloss Class A surfaces can be obtained without painting.
| Original Document | Technical Datasheet(English) | |||
| Features | Toughened/Impact ModifiedHeat ResistanceHigh GlossMirror surfacePaint-freeWeather Resistance | |||
| Additive | Impact Modifier | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
230℃/3.8 kg | *** cm³/10 min | ISO 1133 | |
Water Absorption | *** % | ISO 62 | saturation, 23°C |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C / 50% |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527 | 50 mm/min |
Nominal Tensile Strain at Break | *** % | ISO 527 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | B / 50 |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6/K | ISO 11359 | 0-50 °C |
Glass Transition Temperature | *** °C | ISO 11357 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | IEC 60695-11-10 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.