PLEXIGLAS® Resist zk5BR is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).
Typical properties of impact-modified PLEXIGLAS® molding compounds are:
• high weather resistance
• excellent transmission and clarity
• brilliant appearance
• the pleasant feel and sound of the moldings.
PLEXIGLAS® Resist zk5BR is characterized by the following special properties:
• high break resistance and impact strength
• improved resistance to stress cracking
• balanced property profile
• AMECA listing.
Application:
Used for injection molding as well as for extruding and coextruding panels and profiles
| Original Document | Technical Datasheet(English) | |||
| Resin ID | PMMA-I | |||
| Features | Toughened/Impact ModifiedLight TransmissionGood SurfaceWeather Resistance | |||
| Additive | Impact Modifier | |||
| Appearance | Pellets/GranulesClear/Transparent | |||
| Processing | InjectionExtrusionSheet ExtrusionProfile ExtrusionCo-extrusion | |||
| Compliance | AMECA | |||
| Diagrams | Viscosity-shear rateShearstress-shear rateDynamic Shear modulus (G storage)-temperatureStress-strainSecant modulus-strainStress-strain (isochronous)(Creep) 23°CCreep modulus-time 23°CSpec. enthalpy/mass-temp. (DSC)(Tm = 109 °C)Tensile modulus-temperature | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
230℃/3.8 kg | *** cm³/10 min | ISO 1133 | |
Water Absorption | *** % | ISO 62 | saturation, 23°C |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C / 50% |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527 | 50 mm/min |
Nominal Tensile Strain at Break | *** % | ISO 527 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | B / 50 |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6/K | ISO 11359 | 0-50 °C |
Glass Transition Temperature | *** °C | ISO 11357 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | IEC 60695-11-10 | |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Light Transmission | *** % | ISO 13468-2 | 3mm, D65 |
Haze | *** % | ASTM D1003 | 3mm |
Refractive Index | *** - | ISO 489 | 3mm, 589nm/23°C |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.