PLEXIGLAS® Resist AG 100 is an amorphous thermoplastic molding compound, based on impact-modified polymethyl methacrylate (PMMA).
PLEXIGLAS® molding compounds have the following typical properties:
•high weather resistance
•excellent transmission and clarity
•brilliant appearance
•low weight
•100% recyclable
•pleasant feel and sound of molded parts
PLEXIGLAS® Resist AG 100 is characterized by the following additional properties:
•highest breaking strength and impact strength
•improved resistance to stress cracking
•balanced property profile
•clear reduction of reversible haze at very high and low temperatures
•increased heat deflection temperature under load
•AMECA listing, CAMPUS and moldflow data available
Application:
PLEXIGLAS® Resist AG 100 has a balanced property profile and is used for extruding and coextruding sheets and profiles as well as for injection molding.
| Original Document | Technical Datasheet(English) | |||
| Resin ID | PMMA-I | |||
| Features | Toughened/Impact ModifiedHeat ResistanceLight TransmissionGood SurfaceWeather Resistance | |||
| Additive | Impact Modifier | |||
| Appearance | Pellets/GranulesClear/Transparent | |||
| Processing | InjectionExtrusionSheet ExtrusionProfile ExtrusionCo-extrusion | |||
| Compliance | AMECA | |||
| Diagrams | Viscosity-shear rateShearstress-shear rateStress-strain (isochronous)(Creep) 23°CCreep modulus-time 23°CTensile modulus-temperature | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
230℃/3.8 kg | *** cm³/10 min | ISO 1133 | |
Water Absorption | *** % | ISO 62 | saturation, 23°C |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C / 50% |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527 | 50 mm/min |
Nominal Tensile Strain at Break | *** % | ISO 527 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | B / 50 |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6/K | ISO 11359 | 0-50 °C |
Glass Transition Temperature | *** °C | ISO 11357 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | IEC 60695-11-10 | |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Light Transmission | *** % | ISO 13468-2 | 3mm, D65 |
Haze | *** % | ASTM D1003 | 3mm |
Refractive Index | *** - | ISO 489 | 3mm, 589nm/23°C |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.