PLEXIGLAS® 7N is an amorphous thermoplastic molding compound (PMMA).
Typical properties of PLEXIGLAS® molding compounds are:
• good flow
• high mechanical strength, surface hardness and mar resistance
• high light transmission
• very good weather resistance
• free colorability due to crystal clarity.
Special properties of PLEXIGLAS® 7N molding compound are:
• very good mechanical properties
• high heat deflection temperature
• very good flow / melt viscosity
• AMECA listing.
Application:
Used for injection molding optical and technical items.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热透光易着色耐刮擦耐候性良好流动性 | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | AMECA(美国加拿大汽车认证) | |||
| 曲线坐标点 | N粘度-剪切速度剪切应力-剪切速率动态剪切模量 (G 储能)-温度应力-应变正割模量-应变应力-应变 (等时的) 23°C蠕变模量-时间 23°C拉伸模量-温度 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 6 cm³/10 min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 73 Mpa | ISO 527 | 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 3.5 % | ISO 527 | 5 mm/min |
拉伸模量 | 3200 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 20 kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 100 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 95 °C | ISO 75 | |
维卡软化温度(Vicat) | 103 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
- | 80 E-6/K | ISO 11359 | 0 - 50°C |
玻璃化温度(Tg) | 110 °C | ISO 11357 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | IEC 60695-11-10 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 92 % | ISO 13468-2 | 3 mm, D65 |
雾度 | 0.5 % | ASTM D1003 | 3 mm |
折射率 | 1.49 - | ISO 489 | 3 mm, 589nm/23°C |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。