ELCRES XD2322 polycarbonate (PC) copolymer resin is a UV stabilized opaque grade. This resin offers UL94 V0@1.5mm flame retardancy based on non-bromine, non-chlorine FR system, excellent low temperature ductility characteristics and processability. ELCRES XD2322 resin is an excellent candidate for a wide range of applications such as electronic vehicles (EV) and 5G devices.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐低温冲击阻燃无氯无溴易成型抗紫外线耐候性共聚物 | |||
| 添加助剂 | 阻燃剂紫外线稳定剂 | |||
| 成型方式 | 注塑 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.19 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 15 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 16 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | |
横向(Across Flow) | 0.4~0.8 % | Internal | |
吸水率 | 0.4 % | ISO 62-1 | 23°C/saturated |
吸湿率 | 0.15 % | ISO 62-4 | 23°C/50% RH/Equilibrium |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 58 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 56 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 57 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 59 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6 % | ISO 527 | 50 mm/min |
断裂(brk) | 112 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 108 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
- | 92 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 87 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2400 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2100 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2100 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2000 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 360 J/m | ASTM D256 | |
-30℃ (-22℉) | 652 J/m | ASTM D256 | |
-30℃ (-22℉) | 29 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 780 J/m | ASTM D256 | |
23℃ (73℉) | 63 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 66 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 123 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 118 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 140 °C | ASTM D1525 | Rate B/50 |
相对温度指数(RTI) | |||
冲击Imp,- | 115 °C | UL 746B | |
电气Elec,- | 125 °C | UL 746B | |
强度Str,- | 125 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 61 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 62 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.5 mm | UL94 | |
5VA | 3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
1.5mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
1.5mm | 825 °C | IEC 60695-2-13 | |
紫外线暴露,水暴露试验和浸渍 | F1 - | UL 746C | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相对漏电起痕指数(CTI ) | |||
- | 150 V | IEC 60112 | M |
- | 3 PLC | UL 746A | |
热线圈起燃性(HWI) | 3 PLC | UL 746A | 1.5mm |
热线圈起燃性(HWI) | 2 PLC | UL 746A | 3mm |
高电流电弧起燃性(HAI) | 1 PLC | UL 746A | 1.5mm |
高电流电弧起燃性(HAI) | 0 PLC | UL 746A | 3mm |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。