PC/ABS blend, injection molding grade that poses a good combination of impact, stiffness and toughness. Vicat B120 = 130ºC
Major Benefits
. Easy flow
. Very high impact up to -40ºC
. Low emission grade
. UV stabilized grade
. Good stability even with high humidity conditions
. Low shrinkage
. Good paintability
. Thin-walled parts
Chemical composition
Thermoplastic polymer blend based on polycarbonate (PC) and acrylonitrile-butadienestyrene (ABS).
| Original Document | Technical Datasheet(English) | |||
| Features | High ImpactHigh Impact at Low TemperaturLow ShrinkageGood PaintablilityLow EmissionUV Stabiltiy | |||
| Additive | UV-Stabilizer | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 25ºC |
Melt Volume Flow Rate(MVR) | |||
260°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | |||
230°C/3.8 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294-4 | 60x60x2 mm |
Across Flow | ***~*** % | ISO 294-4 | 60x60x2 mm |
Water Absorption | *** % | ISO 62 | 23ºC, 50 % r.h. |
Water Absorption | *** % | ISO 62 | Water at 23 ºC |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** psi | ASTM D638 | 5 mm/min |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 5 mm/min |
Yield | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 50 mm/min |
Break | *** % | ASTM D638 | 5 mm/min |
Break | *** % | ISO 527-1/-2 | 50 mm/min |
Flexural Modulus | *** psi | ASTM D790 | 1.3 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 180/1A | |
-30℃ (-22℉) | *** J/m | ASTM D256 | 3.2mm |
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | |
23℃ (73℉) | *** J/m | ASTM D256 | 3.2mm |
23℃ (73℉) | *** J/m | ASTM D256 | 6.4mm |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | annealed 4h/80ºC |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | annealed 4h/80ºC |
Vicat Softening Temperature(VST) | *** °F | ASTM D1525 | B50; 50ºC/h |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | B50;50ºC/h |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B120 | B120;120ºC/h |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | |
Across Flow | *** E-6/K | ISO 11359-1/-2 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
Burning Rate | *** mm/min | ISO 3795 | 200x105x2mm |
| Additional Information | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Fogging | |||
- | *** µg/g | VDA 278 | 23ºC,FOG total emission |
Volatile Organic Compounds | *** µgC/g | VDA 277 | 23ºC,Total carbon emission |
Volatile Organic Compounds | *** µg/g | VDA 278 | 23ºC |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.