AKROTEK® PK-VM GF 30 natural (4706) is a 30% glass fibre reinforced Polyketone with high stiffness and strength. Due to its very good media resistance, the material is suitable for use in applications that carry cooling water.
Typical applications
Components in mechanical engineering and the automotive industry.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityChemical ResistanceHydrolysis ResistanceMedia resistantFilled & Reinforced | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23°C |
Melt Volume Flow Rate(MVR) | |||
240℃/2.16 kg | ***~*** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294-4 | |
Across Flow | ***~*** % | ISO 294-4 | |
Moisture /Humidity Absorption | ***~*** % | ISO 1110 | 70°C, 62% r.H. |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | Cond., 1 mm/min |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry, 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2 | Cond., 5 mm/min |
Break | *** Mpa | ISO 527-2 | Dry, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | Cond., 5 mm/min |
Break | *** % | ISO 527-2 | Dry, 5 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Dry, 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 179-1/1eA | Dry |
-30℃ (-22℉) | *** kJ/m² | ISO 179-1/1eA | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | DSC, 10K/min |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
1.6mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
1.6mm | *** °C | IEC 60695-2-13 | |
FMVSS | *** pass | FMVSS 302 | > 1 mm Thickness |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 60093 | Cond. |
Volume Resistivity | *** Ohm-cm | IEC 60093 | Dry |
Volume Resistivity | *** Ohm-cm | IEC 62631-3-1 | Cond. |
Volume Resistivity | *** Ohm-cm | IEC 62631-3-1 | Dry |
Surface Resistivity | *** Ohm | IEC 62631-3-2 | Cond. |
Surface Resistivity | *** Ohm | IEC 62631-3-2 | Dry |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.