VALOX 553 is a 30% glass filled flame retardant Polybutylene Terephthalate/Polycarbonate (PBT/PC) injection moldable grade. It has excellent chemical resistance and a UL94V0@0.86mm and 5VA@2.3mm flame rating. This is a good candidate for applications needing reduced shrinkage/warpage including appliance handles, spotlights, electric motors, and pump housings
| 原厂资料 | 物性表(英文) | |||
| 供应市场 | 亚洲 | |||
| 产品特性 | 阻燃低翘曲低收缩耐化学性填充增强 | |||
| 添加助剂 | 阻燃剂 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 30% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.59 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.3~0.5 % | Internal | flow, 1.5-3.2 mm |
纵向(Flow) | 0.5~0.8 % | Internal | flow, 3.2-4.6 mm |
横向(Across Flow) | 0.4~0.6 % | Internal | xflow, 1.5-3.2 mm |
横向(Across Flow) | 0.6~0.9 % | Internal | xflow, 3.2-4.6 mm |
吸水率 | 0.07 % | ASTM D570 | |
比容 | 0.64 cm³/g | ASTM D792 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 110 Mpa | ASTM D638 | Type I, 5 mm/min |
弯曲强度 | |||
断裂(brk) | 179 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 9400 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 85 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 640 J/m | ASTM D4812 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 118 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 204 °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 138 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 160 °C | ASTM D648 | 6.4 mm, unannealed |
相对温度指数(RTI) | |||
冲击Imp,- | 110 °C | UL 746B | |
电气Elec,- | 125 °C | UL 746B | |
强度Str,- | 125 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 23 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 21.6 E-6/°C | ASTM E831 | 60°C to 138°C, flow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.86 mm | UL94 | |
5VA | 2.3 mm | UL94 | |
氧指数(LOI) | 37.1 % | ASTM D 2863 | |
紫外线暴露,水暴露试验和浸渍 | F1 - | UL 746C | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 4.3E+16 Ohm-cm | ASTM D257 | |
介电常数(DK) | |||
100Hz | 3.8 - | ASTM D 150 | |
1MHz | 3.7 - | ASTM D 150 | |
耗散因数(DF) | |||
100Hz | 20 E-4 | ASTM D 150 | |
1MHz | 200 E-4 | ASTM D150 | |
相对漏电起痕指数(CTI ) | |||
- | 3 PLC | UL 746A | |
绝缘强度 | 18.9 kV/mm | ASTM D149 | in air, 3.2 mm |
绝缘强度 | 25 kV/mm | ASTM D149 | in oil, 1.6 mm |
耐电弧性 | 6 PLC | ASTM D495 | |
高电压电弧起痕速率(HVTR) | 3 PLC | UL 746A | |
热线圈起燃性(HWI) | 1 PLC | UL 746A | |
高电流电弧起燃性(HAI) | 3 PLC | UL 746A |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。