AKROMID® B3 GF 50 S1 natural (3694) is a 50% glass fiber reinforced, impact modified Polyamide 6. It is characterised by very high stiffness and strength as well as a higher notched impact strength compared to a standard PA 6 GF 50. The material is therefore perfectly suitable for industrial applications and for housings and covers in the automotive industry. The material has a light inherent color.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityToughened/Impact ModifiedFilled & Reinforced | |||
| Additive | Impact Modifier | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Reinforced | 50% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23°C |
Moisture /Humidity Absorption | *** % | ISO 1110 | 70°C, 62% r.H. |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | Cond., 1 mm/min |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry, 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2 | Cond., 5 mm/min |
Break | *** Mpa | ISO 527-2 | Dry, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | Cond., 5 mm/min |
Break | *** % | ISO 527-2 | Dry, 5 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179-1/1eA | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179-1/1eU | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | DSC, 10K/min |
Temperature index (TI)-Tensile Strength | |||
20000 h | *** °C | IEC 60216 | 50% loss |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
FMVSS | *** pass | FMVSS 302 | > 1 mm Thickness |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.