AKROMID® A3 1 FR black (3051) is an unreinforced, flame retardant and heat stabilised PA6.6. Listed to UL 94 in allcolours, the material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for switches, housing and fasteners in the electric industry.
| Original Document | Technical Datasheet(English) | |||
| Features | Heat StabilizedFlame RetardantHalogen FreeNon Red Phosphorus | |||
| Additive | Flame RetardantHeat Stabilizer | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294-4 | |
Across Flow | ***~*** % | ISO 294 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | Cond., 1 mm/min |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry, 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2 | Cond., 50 mm/min |
Yield | *** Mpa | ISO 527-2 | Dry, 50 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | Cond., 50 mm/min |
Break | *** % | ISO 527-2 | Dry, 50 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | DSC, 10K/min |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
Oxygen Index | *** % | ISO 4589 | |
Glow Wire Flammability Index(GWFI) | |||
0.4mm | *** °C | IEC 60695-2-12 | |
0.8mm | *** °C | IEC 60695-2-12 | |
1.6mm | *** °C | IEC 60695-2-12 | |
3.2mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
0.4mm | *** °C | IEC 60695-2-13 | |
0.8mm | *** °C | IEC 60695-2-13 | |
1.6mm | *** °C | IEC 60695-2-13 | |
3.2mm | *** °C | IEC 60695-2-13 | |
FMVSS | *** pass | FMVSS 302 | > 1 mm Thickness |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | |
Hot Wire Ignition(HWI) | *** PLC | UL 746A | 0,8mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746A | 0,8mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.