AKROMID® S3 GF 50 1 natural (3533) is a 50% glass fibre reinforced, heat stabilised polyamide 6.10 with very high stiffness and strength as well as lower moisture absorption, high chemical resistance and light inherent color.
Typical applications
Precision parts for apparatus engineering and precision mechanics as well as connectors, housings etc. in the automotive industry.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityHeat StabilizedBio-basedChemical ResistanceLow Moisture AbsorptionFilled & Reinforced | |||
| Additive | Heat Stabilizer | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Reinforced | 50% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23°C |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Moisture /Humidity Absorption | *** % | ISO 1110 | 70°C, 62% r.H. |
Biobased content | *** % | - | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | Cond., 1 mm/min |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry, 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2 | Cond., 5 mm/min |
Break | *** Mpa | ISO 527-2 | Dry, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | Cond., 5 mm/min |
Break | *** % | ISO 527-2 | Dry, 5 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Dry, 2 mm/min |
Flexural Strain | |||
break | *** % | ISO 178 | Dry, 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179-1/1eA | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179-1/1eU | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Dry |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Ball Indentation Hardness | *** Mpa | ISO 2039-1 | 961N/30s |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | |
8 Mpa (1160 psi)（81.6kg/cm²） | *** °C | ISO 75/C | |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | DSC, 10K/min |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
FMVSS | *** pass | FMVSS 302 | > 1 mm Thickness |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.