AKROMID® C3 GF 35 5 XTC black (6680) is a 35% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance. This product version was optimised for laser marking.
Typical applications
Technical parts in mechanical engineering and automotive industry
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityHeat ResistanceHeat StabilizedLaser MarkableFilled & Reinforced | |||
| Additive | Heat Stabilizer | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Reinforced | 35% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23°C |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294-4 | |
Across Flow | ***~*** % | ISO 294-4 | |
Moisture /Humidity Absorption | ***~*** % | ISO 1110 | 70°C, 62% r.H. |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | Cond., 1 mm/min |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry, 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2 | Cond., 5 mm/min |
Break | *** Mpa | ISO 527-2 | Dry, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | Cond., 5 mm/min |
Break | *** % | ISO 527-2 | Dry, 5 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | 23°C to 80°C |
Across Flow | *** E-6/K | ISO 11359-1/-2 | 23°C to 80°C |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | DSC, 10K/min |
Temperature index (TI)-Tensile Strength | |||
5000 h | ***~*** °C | IEC 60216 | 50% loss |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
FMVSS | *** pass | FMVSS 302 | > 1 mm Thickness |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.