AKROMID® C3 GF 30 1 FR black (7243) is a 30 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend. Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved. This grade is also suitable E&E applications (e.g. control cabinets) as well as for railroad applications and meets the requirements for public transportation (EN 45545-2 R22/23/24 HL3).
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定阻燃无卤无红磷良好表面良好流动性填充增强 | |||
| 添加助剂 | 阻燃剂热稳定剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | EN 45545(欧盟轨道交通防火测试) | |||
| 增强填充 | 30% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.42 g/cm³ | ISO 1183 | 23°C |
收缩率 | |||
纵向(Flow) | 0.1~0.3 % | ISO 294-4 | |
横向(Across Flow) | 0.6~0.8 % | ISO 294-4 | |
螺旋流 | 460 mm | - | 2mm Thickness |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 105 Mpa | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) | 148 Mpa | ISO 527-2 | Dry, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 3.9 % | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) | 3 % | ISO 527-2 | Dry, 5 mm/min |
拉伸模量 | 7500 Mpa | ISO 527-2 | Cond., 1 mm/min |
拉伸模量 | 10800 Mpa | ISO 527-2 | Dry, 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 74 kJ/m² | ISO 179-1/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 251 °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 225 °C | ISO 75/A | |
8 Mpa (1160 psi)（81.6kg/cm²） | 168 °C | ISO 75/C | |
熔融温度(Tm) | 262 °C | ISO 11357-3 | DSC, 10K/min |
球压痕温度 | 210 °C | IEC 60695-10-2 | |
温度指数(TI)-拉伸强度 | |||
5000 h | 155 °C | IEC 60216 | 50% loss of tensile strength |
20000 h | 130 °C | IEC 60216 | 50% loss of tensile strength |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.4 mm | UL94 | |
V-0 | 0.8 mm | UL94 | |
V-0 | 1.6 mm | UL94 | |
V-0 | 3.2 mm | UL94 | |
5VA | 1.6 mm | UL94 | |
5VA | 3.2 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
0.4mm | 960 °C | IEC 60695-2-12 | |
0.8mm | 960 °C | IEC 60695-2-12 | |
1.6mm | 960 °C | IEC 60695-2-12 | |
3.2mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
0.4 mm | 725 °C | IEC 60695-2-13 | |
0.8mm | 725 °C | IEC 60695-2-13 | |
1.6mm | 725 °C | IEC 60695-2-13 | |
3.2mm | 725 °C | IEC 60695-2-13 | |
FMVSS | + pass | FMVSS 302 | > 1 mm Thickness |
欧洲轨道车辆认证 | 3 HL | EN 45545-2 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相对漏电起痕指数(CTI ) | |||
溶液A | 600 V | IEC 60112 | |
绝缘强度 | 24 kV/mm | IEC 60243 | 3 mm |
高电压电弧起痕速率(HVTR) | 0 PLC | UL 746A | |
热线圈起燃性(HWI) | 0 PLC | UL 746A | 0,4mm |
热线圈起燃性(HWI) | 0 PLC | UL 746A | 0,8mm |
热线圈起燃性(HWI) | 0 PLC | UL 746A | 1,6mm |
热线圈起燃性(HWI) | 0 PLC | UL 746A | 3,2mm |
高电流电弧起燃性(HAI) | 0 PLC | UL 746A | 0,4mm |
高电流电弧起燃性(HAI) | 0 PLC | UL 746A | 0,8mm |
高电流电弧起燃性(HAI) | 0 PLC | UL 746A | 1,6mm |
高电流电弧起燃性(HAI) | 0 PLC | UL 746A | 3,2mm |
斜面漏电起痕 | 1 kV | ASTM D2303 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。