AKROMID® A3 GF 30 FR EN black (6654) is a PA66 with 30% glass-fibers and flame retardant free of halogens and red phosporous. The product contains an organic stabilization package and is optimized for use in electronic and electric applications.
This formulation has been listed at UL under the name AKROMID® A3 GF 30 FR black (7751). Please consider AKROMID® A3 GF 30 FR black (7751), in case EN quality is not explicitly necessary, because EN requires additional effort and testing.
Typical applications
circuit breaker and housings in E&E industry.
| Original Document | Technical Datasheet(English) | |||
| Features | Flame RetardantHalogen FreeNon Red PhosphorusFilled & Reinforced | |||
| Additive | Flame Retardant | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23°C |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294-4 | |
Across Flow | ***~*** % | ISO 294 | |
Water Absorption | ***~*** % | ISO 62 | 23°C saturated |
Moisture /Humidity Absorption | ***~*** % | ISO 1110 | 70°C, 62% r.H. |
Spiral Flow | *** mm | - | 1mm Thickness |
Spiral Flow | *** mm | - | 2mm Thickness |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | Cond., 1 mm/min |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry, 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2 | Cond., 5 mm/min |
Break | *** Mpa | ISO 527-2 | Dry, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | Cond., 5 mm/min |
Break | *** % | ISO 527-2 | Dry, 5 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Dry, 2 mm/min |
Flexural Strain | |||
break | *** % | ISO 178 | Dry, 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179-1/1eA | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179-1/1eU | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | 23°C to 80°C |
Across Flow | *** E-6/K | ISO 11359-1/-2 | 23°C to 80°C |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | DSC, 10K/min |
Temperature index (TI)-Tensile Strength | |||
5000 h | *** °C | IEC 60216 | 50% loss of tensile strength |
20000 h | *** °C | IEC 60216 | 50% loss of tensile strength |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
0.4mm | *** °C | IEC 60695-2-12 | |
0.8mm | *** °C | IEC 60695-2-12 | |
1.6mm | *** °C | IEC 60695-2-12 | |
3.2mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
0.4mm | *** °C | IEC 60695-2-13 | |
0.8mm | *** °C | IEC 60695-2-13 | |
1.6mm | *** °C | IEC 60695-2-13 | |
3.2mm | *** °C | IEC 60695-2-13 | |
FMVSS | *** pass | FMVSS 302 | > 1 mm Thickness |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 60093 | Cond. |
Volume Resistivity | *** Ohm-cm | IEC 60093 | Dry |
Volume Resistivity | *** Ohm-cm | IEC 62631-3-1 | Cond. |
Volume Resistivity | *** Ohm-cm | IEC 62631-3-1 | Dry |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | |
Hot Wire Ignition(HWI) | PLC | UL 746A | 0,4mm |
Hot Wire Ignition(HWI) | PLC | UL 746A | 0,8mm |
Hot Wire Ignition(HWI) | PLC | UL 746A | 1,6mm |
Hot Wire Ignition(HWI) | PLC | UL 746A | 3,2mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746A | 0,4mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746A | 0,8mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746A | 1,6mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746A | 3,2mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.