AKROMID® C3 1 FR black (5266) is a unreinforced, flame retardant and heat stabilised PA6/6.6 blend. Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved and it is quite suitable for film hinges. This grade meets the requirements for public transportation (EN 45545-2 and ISO 4589-2) and is also suitable for applications in the automotive and E&E markets.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定阻燃无卤无红磷良好表面良好流动性 | |||
| 添加助剂 | 阻燃剂热稳定剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | EN 45545(欧盟轨道交通防火测试) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.16 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 1.2 % | ISO 294-4 | |
横向(Across Flow) | 1.4 % | ISO 294 | |
吸湿率 | 2.1~2.3 % | ISO 1110 | 70°C, 62% r.H. |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 40 Mpa | ISO 527-2 | Cond., 50 mm/min |
屈服(yld) | 75 Mpa | ISO 527-2 | Dry, 50 mm/min |
拉伸延伸率 | |||
断裂(brk) | 50 % | ISO 527-2 | Cond., 50 mm/min |
断裂(brk) | 10 % | ISO 527-2 | Dry, 50 mm/min |
拉伸模量 | 1300 Mpa | ISO 527-2 | Cond., 1 mm/min |
拉伸模量 | 3400 Mpa | ISO 527-2 | Dry, 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 3 kJ/m² | ISO 179-1/1eA | Dry |
23℃ (73℉) | 4 kJ/m² | ISO 179-1/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 90 kJ/m² | ISO 179-1/1eU | Dry |
23℃ (73℉) | NB kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) | NB kJ/m² | ISO 179-1/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 210 °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 70 °C | ISO 75/A | |
熔融温度(Tm) | 260 °C | ISO 11357-3 | DSC, 10K/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.4 mm | UL94 | |
V-0 | 0.8 mm | UL94 | |
V-0 | 1.6 mm | UL94 | |
V-0 | 3.2 mm | UL94 | |
氧指数(LOI) | 34.5 % | ISO 4589 | |
灼热丝可燃性指数(GWFI) | |||
0.4mm | 960 °C | IEC 60695-2-12 | |
0.8mm | 960 °C | IEC 60695-2-12 | |
1.6mm | 960 °C | IEC 60695-2-12 | |
3.2mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
0.4 mm | 750 °C | IEC 60695-2-13 | |
0.8mm | 750 °C | IEC 60695-2-13 | |
1.6mm | 750 °C | IEC 60695-2-13 | |
3.2mm | 775 °C | IEC 60695-2-13 | |
欧洲轨道车辆认证 | 3 HL | EN 45545-2 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相对漏电起痕指数(CTI ) | |||
溶液A | 600 V | IEC 60112 | |
绝缘强度 | 10 kV/mm | IEC 60243 | 3 mm |
高电压电弧起痕速率(HVTR) | 0 PLC | UL 746A | |
热线圈起燃性(HWI) | 4 PLC | UL 746A | 0,4mm |
热线圈起燃性(HWI) | 4 PLC | UL 746A | 0,8mm |
热线圈起燃性(HWI) | 0 PLC | UL 746A | 1,6mm |
热线圈起燃性(HWI) | 0 PLC | UL 746A | 3,2mm |
高电流电弧起燃性(HAI) | 0 PLC | UL 746A | 0,4mm |
高电流电弧起燃性(HAI) | 0 PLC | UL 746A | 0,8mm |
高电流电弧起燃性(HAI) | 0 PLC | UL 746A | 1,6mm |
高电流电弧起燃性(HAI) | 0 PLC | UL 746A | 3,2mm |
斜面漏电起痕 | 1 kV | ASTM D2303 |