AKROLOY® PA GF 50 8 natural (6606) is a 50% glass fibre reinforced, cold water resistant, semi-aromatic polyamide blend with very high stiffness and strength, as well as reduced moisture absorption, modified for the respective application.
Components with tight dimensional tolerances even under high mechanical load, especially in drinking water industry. It is a very cost effective alternative for zinc- and aluminium diecast alloys.
| Original Document | ||||
| Features | High Stiffness/RigidityDimensional StabilityDrinking Water ContactLow Moisture AbsorptionFilled & Reinforced | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Reinforced | 50% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23°C |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Spiral Flow | *** mm | - | 1.00 mm |
Spiral Flow | *** mm | - | 2.00 mm |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/1 | |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2/5 | |
Tensile Elongation | |||
Break | *** % | ISO 527-2/5 | |
Flexural Modulus | *** Mpa | ISO 178 | 2.0 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 2.0 mm/min |
Flexural Strain | |||
break | *** % | ISO 178 | 2.0 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Unannealed |
8 Mpa (1160 psi)（81.6kg/cm²） | *** °C | ISO 75-2/C | Unannealed |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | 10°C/min |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.