AKROLOY® PA K17 FR black (5762) is a 35% glass fibre reinforced, halogen-free flame retardant PA 66 high temperature-alloy with high stiffness and strength as well as reduced moisture absorption.
The material is certified according to CS/FAR Part 25 §285.853a and listed at AIRBUS
Typical applications
Parts in aviation industry
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityFlame RetardantHalogen FreeLow Moisture AbsorptionFilled & Reinforced | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Compliance | FAA FAR | |||
| Reinforced | 35% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23°C |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294-4 | |
Across Flow | ***~*** % | ISO 294-4 | |
Moisture /Humidity Absorption | ***~*** % | ISO 1110 | 70°C, 62% r.H. |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | Cond., 1 mm/min |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry, 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2 | Cond., 5 mm/min |
Break | *** Mpa | ISO 527-2 | Dry, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | Cond., 5 mm/min |
Break | *** % | ISO 527-2 | Dry, 5 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | DSC, 10K/min |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
0.4mm | *** °C | IEC 60695-2-12 | |
0.8mm | *** °C | IEC 60695-2-12 | |
1.6mm | *** °C | IEC 60695-2-12 | |
3.2mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
0.4mm | *** °C | IEC 60695-2-13 | |
0.8mm | *** °C | IEC 60695-2-13 | |
1.6mm | *** °C | IEC 60695-2-13 | |
3.2mm | *** °C | IEC 60695-2-13 | |
FMVSS | *** pass | FMVSS 302 | > 1 mm Thickness |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.