AKROLOY® PA GF 50 natural (2916) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.
The advanced version of this Product is AKROLOY® PA GF 50 natural (6414) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.
Typical applications
Components with high dimensional stability, independent from moisture content. AKROLOY® PA GF 50 is an alternative for aluminium- and zinc diecast alloys.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityDimensional StabilityFilled & Reinforced | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Reinforced | 50% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23°C |
Melt Volume Flow Rate(MVR) | |||
275°C/5 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | ~*** % | ISO 294-4 | |
Across Flow | ***~*** % | ISO 294-4 | |
Water Absorption | ***~*** % | ISO 62 | |
Moisture /Humidity Absorption | ***~*** % | ISO 1110 | 70°C, 62% r.H. |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | Cond., 1 mm/min |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry, 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2 | Cond., 5 mm/min |
Break | *** Mpa | ISO 527-2 | Dry, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | Cond., 5 mm/min |
Break | *** % | ISO 527-2 | Dry, 5 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Dry, 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179-1/1eA | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179-1/1eU | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Dry |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Ball Indentation Hardness | *** Mpa | ISO 2039-1 | 961N/30s |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | 50°C/50N |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | 23°C to 80°C |
Across Flow | *** E-6/K | ISO 11359-1/-2 | 23°C to 80°C |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | DSC, 10K/min |
Temperature index (TI)-Tensile Strength | |||
5000 h | ***~*** °C | IEC 60216 | 50% loss |
20000 h | ***~*** °C | IEC 60216 | 50% loss |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
FMVSS | *** pass | FMVSS 302 | > 1 mm Thickness |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 60093 | Dry |
Volume Resistivity | *** Ohm-cm | IEC 62631-3-1 | Dry |
Surface Resistivity | *** Ohm | IEC 62631-3-2 | Dry |
Dielectric Constant(Permittivity) | |||
1MHz | *** - | IEC 60250 | |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.