AKROLOY® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthFlame RetardantGood SurfaceCreep ResistantGood FlowFilled & Reinforced | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Reinforced | 35% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23°C |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294-4 | |
Across Flow | ***~*** % | ISO 294-4 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry, 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2 | Dry, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | Dry, 5 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | DSC, 10K/min |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
0.4mm | *** °C | IEC 60695-2-12 | |
0.8mm | *** °C | IEC 60695-2-12 | |
1.6mm | *** °C | IEC 60695-2-12 | |
3.2mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
0.4mm | *** °C | IEC 60695-2-13 | |
0.8mm | *** °C | IEC 60695-2-13 | |
1.6mm | *** °C | IEC 60695-2-13 | |
3.2mm | *** °C | IEC 60695-2-13 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.