LNP THERMOTUF RBX7245 (experimental grade name as ER008352) is a compound based on Recycle Polycarbonate resin containing Non-Brominated & Non-Chlorinated Flame Retardant, with excellent V-0 rating at 0.6mm. Post-Consumer Recycling (PCR) polycarbonate content up to 50%.
| Original Document | Technical Datasheet(English) | |||
| Features | Flame RetardantCl- FreeBr- FreeRecycled Contained | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Volume Flow Rate(MVR) | |||
260°C/2.16 kg | *** cm³/10 min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | |||
260°C/2.16 kg | *** g/10min | ASTM D1238 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | 3.2 mm |
Across Flow | ***~*** % | Internal | 3.2 mm |
Water Absorption | *** % | ISO 62 | 23°C/sat |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C / 50% RH |
Post Consumer Recycled | *** % | Internal | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 5 mm/min |
Tensile Modulus | *** Mpa | ISO 527 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Yield | *** Mpa | ISO 527 | 50 mm/min |
Break | *** Mpa | ISO 527 | 50 mm/min |
Break | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | Type I, 50 mm/min |
Yield | *** % | ISO 527 | 50 mm/min |
Break | *** % | ASTM D638 | Type I, 50 mm/min |
Break | *** % | ISO 527 | 50 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Yield | *** Mpa | ISO 178 | 2 mm/min |
Break | *** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | 80*10*4mm, Cut |
0℃ (32℉) | *** kJ/m² | ISO 179/1eA | 80*10*4mm, Cut |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | 80*10*4mm, Cut |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** J/m | ASTM D256 | |
0℃ (32℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** J/m | ASTM D256 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 3.2 mm, unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B120 | |
Relative Temperature Index(RTI), Imp | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
- | *** °C | UL 746B | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-2 | *** mm | UL94 | Min. |
V-0 | *** mm | UL94 | Min. |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.