HCB9310G is 10%GF reinforce super heat resistance PC/PBT resin. HCB9310G has excellent mechnical strength and high chem-resistance. HCB9310G is mainly used in automobile, household electric product, electrician product, etc
| Original Document | Technical Datasheet-ASTM(English) Technical Datasheet-ISO(English) | |||
| Features | Heat ResistanceChemical ResistanceFilled & Reinforced | |||
| Reinforced | 10% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
250°C/5.0 kg | *** g/10 min | ASTM D1238 | |
250°C/5.0 kg | *** g/10 min | ISO 1133 | |
Mold Shrinkage | |||
- | ***~*** % | ASTM D955 | |
- | ***~*** % | ISO 294 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
- | *** Mpa | ASTM D 638 | |
- | *** Mpa | ISO 527 | 5mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | |
Flexural Modulus | *** Mpa | ASTM D790 | |
Flexural Modulus | *** Mpa | ISO 178 | 2mm/min |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | |
- | *** Mpa | ISO 178 | 2mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179 | |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179 | |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | Unannealed,120℃/h |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 5kg 50℃/h |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 60093 | |
Surface Resistivity | *** Ohm | IEC 60093 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.