Base Polymer
Polyurethane, Estertype
Filler/Additive System
15 % carbon fibres
Special Features
electrically conductive, reduced surface resistivity
Market Segment
Automotive, Machinery
Application Area
various
Typical Applications
functional components
| Original Document | Technical Datasheet(English) Technical Datasheet(Chinese) | |||
| Features | Electrically ConductiveFilled & Reinforced | |||
| Processing | InjectionExtrusion | |||
| Reinforced | 15% Carbon Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | |
Tensile Strength | |||
- | *** Mpa | ISO 527 | |
Tensile Elongation | |||
Break | *** % | ISO 527 | |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Strength | |||
- | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore D hardness | *** D | ISO 868 | 15 sec |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Processing Temperature | ***~*** °C | - | Extrusion |
Processing Temperature | ***~*** °C | - | Injection |
Mould temperature | ***~*** °C | - | Injection |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Surface Resistivity | *** Ohm | IEC 62631-3-2 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.