P6006LS is black compound multimodal high density (classified as PE112 ) specifically designed for pressure Pipe low sagging (LS) applications. It delivers exceptional low sag performance for large-diameter pipes and pressure pipes with low standerd dimension ratio (SDR).
TYPICAL APPLICATIONS
P6006LS is specially developed for pressure pipes for portable water, gas, sewage and other liquids.
| Original Document | Technical Datasheet(English) | |||
| Appearance | Black | |||
| Processing | ExtrusionTube Extrusion | |||
| Reinforced | 2.25% Carbon black | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D 1505 | 23°C |
Melt Mass Flow Rate(MFR) | |||
190℃/5 kg | *** g/10 min | ISO 1133 | |
190℃/21.6 kg | *** g/10 min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | |
Tensile Elongation | |||
Break | *** % | ISO 527 | |
Tensile Creep Modulus | |||
1000h | *** Mpa | ISO 899-1 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179 | |
| Additional Information | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Oxidative Induction Time | *** Min | EN 728 | 210°C |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.