P6006LS is black compound multimodal high density (classified as PE112 ) specifically designed for pressure Pipe low sagging (LS) applications. It delivers exceptional low sag performance for large-diameter pipes and pressure pipes with low standerd dimension ratio (SDR).
TYPICAL APPLICATIONS
P6006LS is specially developed for pressure pipes for portable water, gas, sewage and other liquids.
| 原厂资料 | 物性表(英文) | |||
| 颜色形状 | 黑色 | |||
| 成型方式 | 挤出管材挤出 | |||
| 增强填充 | 2.25% 炭黑 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.96 g/cm³ | ASTM D 1505 | 23°C |
熔体质量流动速率(MFR) | |||
190℃/5 kg | 0.23 g/10 min | ISO 1133 | |
190℃/21.6 kg | 6.4 g/10 min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 23 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 350 % | ISO 527 | |
拉伸模量 | 850 Mpa | ASTM D638 | |
拉伸蠕变模量 | |||
1000h | 360 Mpa | ISO 899-1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 26 kJ/m² | ISO 179 | |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
氧化诱导期(OIT) | 20 Min | EN 728 | 210°C |