P6006 is black compound high density (class MRS 10 - PE 100) Polyethylene with multimodal distribution of molecular mass. It is specifically designed for pressure Pipe applications. It provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength.
TYPICAL APPLICATIONS
P6006 Pressure pipes for drinking water, irrigation, gas distribution and waste water pipes. It is also recommended for manufacture of chemical liners and containers.
| Original Document | Technical Datasheet(English) | |||
| Features | Drinking Water ContactESCRChemical Resistance | |||
| Appearance | Black | |||
| Processing | ExtrusionTube Extrusion | |||
| Reinforced | 2.25% Carbon black | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D 1505 | 23°C |
Melt Mass Flow Rate(MFR) | |||
190℃/5 kg | *** g/10 min | ISO 1133 | |
190℃/21.6 kg | *** g/10 min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | |
23℃ (73℉) | *** kJ/m² | ISO 179 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore D hardness | *** D | ASTM D 2240 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | |
| Additional Information | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Oxidative Induction Time | *** Min | EN 728 | 210°C |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.