SABIC® HDPE M1053 is an easy-to-process, tough grade with good resistance to environmental stress cracking (ESCR) and low notch sensitivity. SABIC® HDPE M1053 is typically used for e.g. caps, closures and pails.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
| Original Document | Technical Datasheet(English) | |||
| Solutions | Tube Shoulder for Cosmetic Tube PackagingHinge Cap for Cosmetic Tube Packaging | |||
| Features | Easy processingESCR | |||
| Applications | Caps/ClosuresPails | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ISO 1133 | |
190℃/5 kg | *** g/10 min | ISO 1133 | |
Environmental Stress Cracking Resistance | *** Hours | Internal | Caps, 10% Igepal CO-630 at 40 °C |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2 | |
Break | *** Mpa | ISO 527-2 | |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Strength | |||
- | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore D hardness | *** D | ISO 868 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 10 N (VST/A) |
Melt Temperature(Tm) | *** °C | ISO 11357-3 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.