SABIC® HDPE FJ01552 is a TNPP free grade. It is a medium molecular weight High Density Polyethylene designed for blown film extrusion. It has a broad molecular weight with excellent extrudability. The design of the product, molecular architecture and density, gives it a unique combination of easy extrusion and strong physical properties which makes it suitable for producing thin films with excellent strength and rigidity.
TYPICAL APPLICATIONS
SABIC® HDPE FJ01552 resin is recommended for the production of strong millinery and notion bags, deep freeze bags, table cloths and thin film as quality replacement for paper products.
| Original Document | Technical Datasheet(English) | |||
| Processing | ExtrusionBlown Film | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D 1505 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ASTM D1238 | |
190℃/21.6 kg | *** g/10 min | ASTM D 1238 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D 882 | MD, 15 μm film |
Yield | *** Mpa | ASTM D 882 | TD, 15 μm film |
Break | *** Mpa | ASTM D 882 | MD, 15 μm film |
Break | *** Mpa | ASTM D 882 | TD, 15 μm film |
Tensile Elongation | |||
Break | *** % | ASTM D 882 | MD, 15 μm film |
Break | *** % | ASTM D 882 | TD, 15 μm film |
Elmondorf Tear | *** g | ASTM D 1922 | MD, 15 μm film |
Elmondorf Tear | *** g | ASTM D 1922 | TD, 15 μm film |
Secant Modulus | *** Mpa | ASTM D 882 | MD, 15 μm film, 1% secant |
Secant Modulus | *** Mpa | ASTM D 882 | TD, 15 μm film, 1% secant |
Dart Drop Impact | *** g/µm | ASTM D 1709 | F50, 15 μm film |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.