HDPE FI0851P is a high molecular weight high density polyethylene resin designed for blown film applications. This resin has broad molecular weight distribution that makes it easier to process. Films made from this resin exhibit high stiffness, excellent impact and toughness characteristics.
| 原厂资料 | 物性表(英文) | |||
| 成型方式 | 吹膜 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.951 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.05 g/10min | ASTM D1238 | |
190℃/21 kg | 8 g/10 min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 126 °C | ASTM D1525 | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 35 Mpa | ASTM D 882 | MD |
屈服(yld) | 30 Mpa | ASTM D 882 | TD |
断裂(brk) | 50 Mpa | ASTM D 882 | MD |
断裂(brk) | 48 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 490 % | ASTM D 882 | MD |
断裂(brk) | 500 % | ASTM D 882 | TD |
埃尔曼多夫撕裂 | 17 g/µm | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 30 g/µm | ASTM D 1922 | TD |
落锤冲击 | 340 g | ASTM D 1709 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。