SUPEER™ Metallocene Linear Low Density Polyethylene (mLLDPE) 8112 is an ethylene-octene copolymer produced via solution polymerization using metallocene catalyst. It performs well in a wide range of general purpose and high performance LLDPE blown film applications and have excellent processability.
TYPICAL APPLICATIONS
Lamination film, frozen bag, liquid pouch, industrial liner, stretch hood, surface protective film.
| Original Document | Technical Datasheet(English) | |||
| Processing | Blown Film | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D 1505 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ASTM D1238 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Melt Temperature(Tm) | *** °C | ASTM D3418 | DSC |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Haze | *** % | ASTM D1003 | |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D 882 | MD, 50 µm film |
Yield | *** Mpa | ASTM D 882 | TD, 50 µm film |
Break | *** Mpa | ASTM D 882 | MD, 50 µm film |
Break | *** Mpa | ASTM D 882 | TD, 50 µm film |
Tensile Elongation | |||
Break | *** % | ASTM D 882 | MD, 50 µm film |
Break | *** % | ASTM D 882 | TD, 50 µm film |
Elmondorf Tear | *** g/µm | ASTM D 1922 | MD, 50 µm film |
Elmondorf Tear | *** g/µm | ASTM D 1922 | TD, 50 µm film |
Secant Modulus | *** Mpa | ASTM D 882 | MD, 50 µm film, 1% secant |
Secant Modulus | *** Mpa | ASTM D 882 | TD, 50 µm film, 1% secant |
Dart Drop Impact | *** g | ASTM D 1709 | F50, 50 µm film |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.