SUPEER™ Metallocene Linear Low Density Polyethylene (mLLDPE) 7118LE is a metallocene ethylene-hexene copolymer. It has a good processability and performs well in a wide range of general purpose and high performance blown film applications. Films produced with this grade offer good tensile and impact strength, puncture resistance and sealing properties.
The resin contains anti-block and slip agent.
SABIC® mLLDPE 7118LE is typically used for applications like heavy duty bags, agriculture film, stretch hood, lamination film, frozen bags. Properties have been measured on blown film of 25 µm (mono layer) and BUR = 2.5
Typical processing conditions for SABIC® mLLDPE 7118LE: processing temperatures 180 - 230 °C.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
| Original Document | Technical Datasheet(English) | |||
| Additive | Slip agentAntiblock | |||
| Processing | Blown Film | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ASTM D1238 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 10 N (VST/A) |
Melt Temperature(Tm) | *** °C | ASTM D3418 | DSC |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Haze | *** % | ASTM D1003 | |
Gloss | *** - | ASTM D 2457 | 45° |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
- | *** Mpa | ASTM D882 | MD |
- | *** Mpa | ASTM D882 | TD |
Tensile Elongation | |||
Break | *** % | ASTM D 882 | MD |
Break | *** % | ASTM D 882 | TD |
Tensile Modulus | *** Mpa | ASTM D 882 | MD |
Tensile Modulus | *** Mpa | ASTM D 882 | TD |
Piercing strength | *** N | ASTM D5748 | Protrusion |
Elmondorf Tear | *** g/µm | ASTM D 1922 | MD |
Elmondorf Tear | *** g/µm | ASTM D 1922 | TD |
Dart Drop Impact | *** g/µm | ASTM D 1709 | F50 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.