COHERE™ Metallocene Polyolefin Plastomer (POP) S400 is an ethylene-octene copolymer produced via solution polymerization using metallocene catalyst. It performs well in high performance flexible packaging applications with excellent toughness, hot tack, hot seal, optical properties and shows enhanced cling force in protection film application.
TYPICAL APPLICATIONS
• Packaging with outstanding sealing performance (low seal initiation temperature, broad hot tack window, excellent seal through contamination).
• Packaging available for high speed form-fill-sealing machine.
• Protection film with enhanced cling force.
• Cling cast stretch film.
| Original Document | Technical Datasheet(English) | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ASTM D1238 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Melt Temperature(Tm) | *** °C | Internal | |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Haze | *** % | ASTM D1003 | |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Break | *** Mpa | ASTM D 882 | MD, 40 µm film |
Break | *** Mpa | ASTM D 882 | TD, 40 µm film |
Tensile Elongation | |||
Break | *** % | ASTM D 882 | MD, 40 µm film |
Break | *** % | ASTM D 882 | TD, 40 µm film |
Elmondorf Tear | *** g/µm | ASTM D 1922 | MD, 40 µm film |
Elmondorf Tear | *** g/µm | ASTM D 1922 | TD, 40 µm film |
Secant Modulus | *** Mpa | ASTM D 882 | MD, 40 µm film, 1% secant |
Secant Modulus | *** Mpa | ASTM D 882 | TD, 40 µm film, 1% secant |
Dart Drop Impact | *** g | ASTM D 1709 | Method A, 40 µm film |
Seal Initiation Temperature | *** ℃ | Internal | 40 µm film |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.