COHERE™ Metallocene Polyolefin Plastomer (POP) 8170D is an ethylene-octene copolymer produced via solution polymerization using metallocene catalyst. It can be used in monolayer or coextruded film to enhance heat-sealing properties, clarity, toughness, flexibility and elasticity. It has strict gel control to meet high quality film requirements.
TYPICAL APPLICATIONS
• Sealant layer in multi-layer film;
• Cling layer in stretch wrap film;
• Adhesive layer in surface protect film.
| Original Document | Technical Datasheet(English) | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | 23°C |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ASTM D1238 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Break | *** Mpa | ASTM D638 | Compression Molded |
at 100% strain | *** Mpa | ASTM D 638 | Compression Molded |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Compression Molded |
Flexural Modulus | *** Mpa | ASTM D790 | 1% Secant |
Tear Strength | *** kN/m | ASTM D 624 | Type C |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Melt Temperature(Tm) | *** °C | Internal |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.