SABIC® PPcompound H1200 is a high impact, halogen free flame retardant, non-filled Polypropylene compounds. It has a UL94 V0@ 2mm flame rating. This material has been designed to combine a good performance profile with good processing and FR characteristics.
IMDS ID:1062970462
| Original Document | Technical Datasheet(English) | |||
| Features | High ImpactFlame RetardantHalogen FreeEasy processing | |||
| Additive | Flame Retardant | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
- | *** % | Internal | 65x65x3.2mm, 24 hours after injection moulding |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527/1A | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527/1A | |
Break | *** Mpa | ISO 527/1A | |
Tensile Elongation | |||
Break | *** % | ISO 527/1A | |
Flexural Modulus | *** Mpa | ISO 178/1A | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6/K | ISO 11359-2 | -30 °C to 100 °C |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.