SABIC® PPcompound G3220AE is a 20% short glass fiber reinforced emission optimized Polypropylene . The base material is a PP homopolymer. The glass fibres are chemically coupled to the PP matrix. This material has been designed to combine a good performance profile with fast processing.
SABIC® PPcompound G3220AE is a designated automotive grade.
IMDS ID: 817176771
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 短周期成型低挥发VOC均聚物填充增强 | |||
| 添加助剂 | 化学偶联剂 | |||
| 增强填充 | 20% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.04 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 17 g/10min | ISO 1133 | |
收缩率 | |||
- | 0.7 % | Internal | 65x65x3.2mm, 24 hours after injection moulding |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 80 Mpa | ISO 527/1A | |
拉伸延伸率 | |||
断裂(brk) | 3.3 % | ISO 527/1A | |
弯曲模量 | 4500 Mpa | ISO 178/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 150 °C | ISO 75/A | |
线性膨胀系数(CLTE) | |||
- | 55 E-6/K | ISO 11359-2 | -30 °C to 100 °C |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。