SABIC® PPcompound 15T1030 is a 30% talc-filled polypropylene homopolymer. Its high modulus and good thermal stabilization makes it suited for applications under the bonnet such as heating, ventilation and air conditioning housings.
SABIC® PPcompound 15T1030 is a designated automotive grade.
IMDS ID: 439230598
| Original Document | Technical Datasheet(English) | |||
| Features | Heat StabilizedHomopolymerFilled & Reinforced | |||
| Additive | Heat Stabilizer | |||
| Reinforced | 30% Talc | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
- | *** % | Internal | 65x65x3.2mm, 24 hours after injection moulding |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527/1A | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527/1A | |
Break | *** Mpa | ISO 527/1A | |
Tensile Elongation | |||
Break | *** % | ISO 527/1A | |
Flexural Modulus | *** Mpa | ISO 178/1A | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-20℃ (-4℉) | *** kJ/m² | ISO 180/1A | |
0℃ (32℉) | *** kJ/m² | ISO 180/1A | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/B | |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6/K | ISO 11359-2 | -30 °C to 100 °C |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.