ICORENE® 1490 is a UV stabilised linear medium density polyethylene colour powder.
It has been developed for use as a powder in rotational moulding.
This grade is a very fast processing material which is very high in ESCR and cold impact strength. It is suitable for use in many different applications but especially where very fast pinhole removal is needed. It is easy to process with a low shrinkage tendency.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好的刚性低收缩易成型抗紫外线ESCR良好流动性 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 颜色形状 | 粉末状 | |||
| 成型方式 | 滚塑 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.936 g/cm³ | ISO 1183 | 23°C |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 12 g/10min | ISO 1133 | |
环境应力开裂(ESCR ) | 500 Hours | ASTM D 1693 | Condition B, 50°C, 10% Igepal, Rotational Molded, F50 |
环境应力开裂(ESCR ) | 1000 Hours | ASTM D 1693 | Condition B, 50°C, 100% Igepal, Rotational Molded, F50 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 17 Mpa | ISO 527 | 23°C |
拉伸延伸率 | |||
断裂(brk) | 450 % | ISO 527-2 | 23°C |
弯曲模量 | 600 Mpa | ISO 178 | 23°C |
拉伸模量 | 700 Mpa | ISO 527-1 | 23°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
落锤冲击 | 200 J/cm | Internal | -20°C, 3.20 mm, Rotomoul |
落锤冲击 | 280 J/cm | ARM | -40°C, Rotomoulding |
拉伸冲击 | 73 kJ/m² | ISO 8256 | -30°C, Notched |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 106 °C | ISO 306/A |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。