PolyAxis LP-8100 is a high density polyethylene intended for the rotational molding industry. This stiff yet tough compound was designed for watercraft products.
| Original Document | Technical Datasheet(English) | |||
| Features | UV Stabiltiy | |||
| Additive | UV-Stabilizer | |||
| Appearance | Pellets/GranulesPowder | |||
| Processing | Rotational Molding | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D 1505 | Compression Molded |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ASTM D1238 | |
Environmental Stress Cracking Resistance | *** Hours | ASTM D 1693 | 10% Igepal, Compression Molded, F50 |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 51 mm/min, Rotational Molded |
Tensile Elongation | |||
Break | *** % | ASTM D638 | 51 mm/min, Rotational Molded |
Flexural Modulus | *** Mpa | ASTM D790 | 1% Secant, Rotational Molded |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Falling Dart Impact | *** J | Internal | -40°C, 3.18 mm, Rotational Molded |
Falling Dart Impact | *** J | Internal | -40°C, 6.35 mm, Rotational Molded |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Unannealed, 3.18 mm, Rotational Molded |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Unannealed, 3.18 mm, Rotational Molded |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.