218WJ is a butene Linear Low Density Polyethylene TNPP free grade suitable for general‐purpose packaging. It is easy to process giving good tensile properties, impact strength and optical properties. 218WJ contains slip and antiblock additives.
TYPICAL APPLICATIONS
Lamination film, thin liners, shopping bags, carrier bags, garbage bags, coextruded films, consumer packaging and other general-purpose applications.
| 原厂资料 | 物性表(英文) | |||
| 添加助剂 | 增滑剂开口剂 | |||
| 成型方式 | 吹膜 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.918 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 2 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 98 °C | ASTM D1525 | |
加工温度 | 185~205 °C | - | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 13 % | ASTM D1003 | 30 μm film |
光泽度 | 80 - | ASTM D 2457 | at 60° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 12 Mpa | ASTM D 882 | MD |
屈服(yld) | 10 Mpa | ASTM D 882 | TD |
断裂(brk) | 35 Mpa | ASTM D 882 | MD |
断裂(brk) | 29 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 700 % | ASTM D 882 | MD |
断裂(brk) | 750 % | ASTM D 882 | TD |
埃尔曼多夫撕裂 | 130 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 320 g | ASTM D 1922 | TD |
割线模量 | 220 Mpa | ASTM D 882 | MD, 1% secant |
割线模量 | 260 Mpa | ASTM D 882 | TD, 1% secant |
落锤冲击 | 85 g/µm | ASTM D 1709 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。