Soarlite™ is reinforced by grass fiber to improve mechanical strength (especially stiffness) and has adjusted viscosity for injection molding. Thanks to these properties, Soarlite™ is used to substitute metal parts to plastic. Additionally, Soarlite™ han anti-statics property due to hydrophilicity so it is used for Timing pulley which generates static electricity.
Application example
・Tape reel (IT parts)
・Timing pulley
・Bobbin guide (spinning)
・Substitution for metal (printing parts)
・Plastic nails etc.
Features of Soarnol™
・High durability comes from high stiffness
・Reduce generation of static electricity
| Original Document | Technical Datasheet(Japanese) | |||
| Features | Anti-Static | |||
| Appearance | Pellets/GranulesTranslucentYellow | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
210℃/2.16kg | *** g/10 min | ASTM D 1238 | |
230°C/2.16 kg | *** g/10min | ASTM D 1238 | |
Molding Shrinkage | |||
- | ***~*** % | Internal | 3.0×100φ |
Water Absorption | *** % | - | 20℃, 66％RH(2000days), Saturation |
Water Absorption | *** % | - | 20℃,immersion, 24hr |
Water Absorption | *** % | - | 37℃ 96％RH 3days |
Abrasion resistance | *** mg/1000cy | Internal | CS-17, 1kg |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 3.2t |
Tensile Strength | |||
- | *** Mpa | ASTM D 638 | 3.2t |
Tensile Elongation | |||
- | *** % | ASTM D 638 | 3.2t |
Flexural Modulus | *** Mpa | ASTM D790 | 6.4×12.7×127 |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | 6.4×12.7×127 |
Flexural Fatigue | *** Mpa | Internal | SCHENCK TYPE 3.0t |
Compressive Strength | *** Mpa | ASTM D 695 | 12.7×12.7×25.4 |
Tensile Set | *** % | Internal | 3.2×12.7×216 |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
- | *** J/m | ASTM D 256 | 12.7×12.7×63.5 |
Izod Unnotched Impact Strengh | |||
- | *** J/m | ASTM D 256 | 12.7×12.7×63.5 |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M | *** M | ASTM D 785 | 3.2×100φ |
Rockwell R | *** R | ASTM D785 | 3.2×100φ |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 12.7×12.7×127 |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 12.7×12.7×127 |
- | *** °C | Internal | Unload |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6/K | ASTM D 696 | Below 70℃ |
Processing Temperature | ***~*** °C | - | |
Mould temperature | ***~*** °C | - | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | 1KV |
Surface Resistivity | *** Ohm | ASTM D257 | 1KV |
Dielectric Constant(Permittivity) | |||
- | *** - | ASTM D150 | |
Dissipation Factor | |||
- | *** E-4 | ASTM D 150 | |
Dielectric Strength | *** kV/mm | ASTM D149 | 3×100×100 |
Arc Resistance | *** sec | ASTM D495 | 3.2×100φ |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.