SoarnoL™ AT4412B is one of the standard grades of SoarnoL™, its ethylene content is 44 mol% with a high MFR (melt flow rate).
SoarnoL™ AT4412B has excellent water resistance and good gas barrier property, especially in high humidity environments. Its gas barrier property is not drastically lower at high humidity.
This resin is primarily used in co-extruded cast film applications, tube and co-extrusion coating applications.
| Original Document | Technical Datasheet(English) Technical Datasheet(Chinese) | |||
| Features | High Barrier property/Low permeation | |||
| Processing | Cast FilmTube ExtrusionExtrusion Coating | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | Internal | 23℃ |
Melt Mass Flow Rate(MFR) | |||
210℃/2.16kg | *** g/10 min | ISO 1133 | |
Total Volatiles | *** % | Internal | |
Ethylene Content | *** % | Internal | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Melt Temperature(Tm) | *** °C | Internal | |
Glass Transition Temperature | *** °C | DSC | 10℃／min |
Freezing temperature | *** °C | DSC | 10℃／min |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Oxygen permeability | *** cc-20µm/m²-day-atm | Internal | 20℃×65%RH |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.