ULTEM 9085 resin is a polyetherimide blend. The material is designed for use in Aerospace cabin interiors but can also be used for FDM printing and in e.g. Rail applications. The material meets Aerospace FAR25.853 and OSU55/55 heat release requirements. It is approved by main Aerospace OEMs. Material has Rail EN45545 R6-HL3 rating. The material may offer excellent flow, stiffness and ductility balance, enabling thin wall lightweight designs. Material is opaque and can be custom colored.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性耐热阻燃尺寸稳定低收缩抗蠕变低烟浓度无(低)毒耐化学性耐水解 | |||
| 颜色形状 | 粒状可定制色不透明色 | |||
| 成型方式 | 注塑挤出片材挤出型材挤出热成型熔丝制造 (FFF)3D打印 | |||
| 法规认证 | EN 45545(欧盟轨道交通防火测试)FAA FAR(美国航空管理局)OSU(热释放测试) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.34 g/cm³ | ISO 1183 | |
比重 | 1.34 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
340°C/5.0 kg | 40 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
295°C/6.6 kg | 8.9 g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | Internal | 3.2 mm |
吸水率 | 0.15 % | ISO 62-1 | 23°C/24hrs |
吸水率 | 0.7 % | ISO 62-1 | 23°C/saturated |
吸湿率 | 0.1 % | ISO 62-4 | 23°C/50% RH/24hrs |
吸湿率 | 0.4 % | ISO 62-4 | 23°C/50% RH/Equilibrium |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 86 Mpa | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 94 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 88 Mpa | ISO 527 | 5 mm/min |
屈服(yld) | 94 Mpa | ISO 527 | 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 7 % | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 7 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6.5 % | ISO 527 | 5 mm/min |
屈服(yld) | 6.7 % | ISO 527 | 50 mm/min |
断裂(brk) | 70 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 70 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 70 % | ISO 527 | 5 mm/min |
断裂(brk) | 70 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 138 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 129 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2800 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2700 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 3000 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 2850 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 8 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 65 J/m | ASTM D256 | |
-30℃ (-22℉) | 8 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 115 J/m | ASTM D256 | |
23℃ (73℉) | 10 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 180/1U | 80*10*4 |
-30℃ (-22℉) | NB J/m | ASTM D 4812 | |
23℃ (73℉) | NB J/m | ASTM D4812 | |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*4 |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 115 M | ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 169 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 169 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 153 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 152 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 173 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 175 °C | ISO 306/B120 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 65 E-6/°C | ASTM E831 | -30°C to 80°C, flow |
纵向(Flow) | 65 E-6/°C | ISO 11359-2 | -30°C to 80°C, flow |
横向(Across Flow) | 70 E-6/°C | ASTM E831 | -30°C to 80°C, xflow |
横向(Across Flow) | 70 E-6/°C | ISO 11359-2 | -30°C to 80°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
氧指数(LOI) | 49 % | ASTM D 2863 | |
垂直燃烧 | 60 sec | FAR 25.853 | PASS |
放热率 | 55 kW/m² | FAR 25.853 | OSU peak heat release rate (5 minute test) |
放热率 | 55 kW-min/m² | FAR 25.853 | OSU total heat release (2 minute test) |
FAA 燃烧性 | 5 - | FAR 25.853 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。