TECHNYL® A 60X1 V25 Natural is a polyamide 66 based on a non-halogenated flame retardant system, reinforced with 25% of glass fiber, heat stabilized, for injection moulding. This grade offers excellent flame retardancy properties (UL94 V0, UL94 5VA, GWIT) combined with excellent processing, mechanical and electrical performance. The data provided are based on laboratory/experimental results. These data could be adjusted after industrial production.
| Original Document | Technical Datasheet(English) | |||
| Features | Flame RetardantHalogen FreeNon Red PhosphorusFilled & Reinforced | |||
| Additive | Flame Retardant | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Compliance | REACH (EC 1907/2006)RoHS | |||
| Reinforced | 25% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
Across Flow | *** % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
Water Absorption | *** % | ISO 62 | 24 hr, 23°C |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | Dry. 1 mm/min |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | cond., 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | Dry |
Break | *** Mpa | ISO 527-1/-2 | cond. |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | Dry |
Break | *** % | ISO 527-1/-2 | cond. |
Flexural Modulus | *** Mpa | ASTM D790 | Dry. 2 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | cond., 2 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Dry. 2 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | cond., 2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Dry. 2 mm/min |
Flexural Strain | |||
- | *** % | ISO 178 | cond., 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | cond. |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | cond. |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/1A | Dry |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | cond. |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | |
Melt Temperature(Tm) | *** °C | ISO 11357-1 | 10°C/min |
Processing Temperature | ***~*** °C | - | |
Mould temperature | ***~*** °C | - | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
5VA | *** mm | UL94 | |
5VA | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
0.75mm | *** °C | IEC 60695-2-12 | |
1.5mm | *** °C | IEC 60695-2-12 | |
3mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
0.75mm | *** °C | IEC 60695-2-13 | |
1.5mm | *** °C | IEC 60695-2-13 | |
3.0mm | *** °C | IEC 60695-2-13 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | |
Surface Resistivity | *** Ohm | IEC 62631-3-2 | |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 | 1 mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.