TECHNYL® ONE J 60X1 V30 Black is a high temperature polyamide based on a non-halogenated flame retardant system, reinforced with 30% of glass fiber with best-in-class fire protection behavior, for injection moulding. A full yellow card is available with a UL94 V0 rating at 0.4 mm, unmatched thermal ageing properties (150°C electrical RTI - Relative Thermal Index), and outstanding electrical properties, including a high comparative tracking index (CTI 0 for 600 volts and higher). This product has superior electrical performance compared to traditional high-performance plastics. Its low corrosion ensures processing tools longevity. This Technyl is laser welding suitable. This product, based on a high fluidity matrix, offers strong benefits in term of productivity and design freedom.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热阻燃无卤无红磷耐电弧性良好表面激光标记易焊接耐腐蚀高流动填充增强 | |||
| 添加助剂 | 热稳定剂 | |||
| 颜色形状 | 粒状本色黑色白色灰色 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | EN 45545(欧盟轨道交通防火测试)REACH (EC 1907/2006)RoHS(欧盟电子电气设备中有害物质) | |||
| 增强填充 | 30% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.41 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.3 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
横向(Across Flow) | 0.95 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
吸水率 | 0.63 % | ISO 62 | 24 hr, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 145 Mpa | ISO 527-1/-2 | Dry. |
断裂(brk) | 110 Mpa | ISO 527-1/-2 | cond. |
拉伸延伸率 | |||
断裂(brk) | 2.5 % | ISO 527-1/-2 | Dry. |
断裂(brk) | 3.3 % | ISO 527-1/-2 | cond., 2 mm/min |
弯曲强度 | |||
- | 230 Mpa | ISO 178 | Dry. 2 mm/min |
- | 185 Mpa | ISO 178 | cond., 2 mm/min |
弯曲模量 | 9000 Mpa | ISO 178 | Dry. 2 mm/min |
弯曲模量 | 8000 Mpa | ISO 178 | cond., 2 mm/min |
拉伸模量 | 11000 Mpa | ISO 527-1/-2 | Dry. 1 mm/min |
拉伸模量 | 9100 Mpa | ISO 527-1/-2 | cond., 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 9 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 9 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | cond. |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 50 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 55 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 62 kJ/m² | ISO 179/1eU | cond. |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 9.5 kJ/m² | ISO 180/1A | Dry |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 55 kJ/m² | ISO 180/1U | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 274 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 257 °C | ISO 75 | |
熔融温度(Tm) | 280 °C | ISO 11357-1 | 10°C/min |
加工温度 | 285~300 °C | - | |
模具温度 | 90~110 °C | - | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.4 mm | UL94 | |
5VA | 0.75 mm | UL94 | |
5VA | 1.5 mm | UL94 | |
5VA | 3 mm | UL94 | |
氧指数(LOI) | 45 % | ISO 4589 | |
灼热丝可燃性指数(GWFI) | |||
0.75mm | 960 °C | IEC 60695-2-12 | |
1.5mm | 960 °C | IEC 60695-2-12 | |
3mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
0.75mm | 800 °C | IEC 60695-2-13 | |
1.5mm | 800 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | IEC 62631-3-1 | |
表面电阻率 | 2.0E+15 Ohm | IEC 62631-3-2 | |
相对漏电起痕指数(CTI ) | |||
溶液A | 600 V | IEC 60112 | |
绝缘强度 | 35 kV/mm | IEC 60243-1 | 1 mm |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。