TECHNYL® C 52G1 V20 Grey R7035 CF is a polyamide 6 based on a non-phosphorous and non-halogenated flame retardant system, reinforced with 20% of glass fiber, heat stabilized, for injection moulding. This is a flame retardant grade with excellent moulding and electrical performance.
| Original Document | Technical Datasheet(English) | |||
| Features | Heat StabilizedFlame RetardantHalogen FreeNon Red PhosphorusFilled & Reinforced | |||
| Additive | Flame RetardantHeat Stabilizer | |||
| Appearance | Pellets/GranulesWhiteGray Color | |||
| Processing | Injection | |||
| Compliance | EN 45545REACH (EC 1907/2006)RoHS | |||
| Reinforced | 20% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Water Absorption | *** % | ISO 62 | 24 hr, 23°C |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | Dry. 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | Dry |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | |
Melt Temperature(Tm) | *** °C | ISO 11357-1 | 10°C/min |
Processing Temperature | ***~*** °C | - | |
Mould temperature | ***~*** °C | - | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-2 | *** mm | UL94 | |
V-2 | *** mm | UL94 | |
V-2 | *** mm | UL94 | |
Oxygen Index | *** % | ISO 4589 | |
Glow Wire Flammability Index(GWFI) | |||
0.75mm | *** °C | IEC 60695-2-12 | |
1.5mm | *** °C | IEC 60695-2-12 | |
3mm | *** °C | IEC 60695-2-12 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 | 1 mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.