TECHNYL® RED J 218HP V50 BLACK 21N is a co-polyamide 66/6T reinforced with 50% glass fibre, heat stabilized, for injection moulding. This grade offers outstanding long-term heat ageing performance of up to 220°C for 2000 hours or 210°C for 3000 hours in addition to strength and stiffness at use temperature higher than 35% glass fiber grades. TECHNYL RED J shows high chemical resistance, easy processing and excellent surface aspect. In addition, TECHNYL RED J delivers high burst pressure levels confirmed in extensive pulsated hot air pressure tests at TECHNYL HUB test center. Recommended melt and mold temperatures are significantly lower than competitive PA4.6 or PPA resins, which saves energy during processing and minimizes part cooling time. The data provided are based on laboratory / experimental results and could be adjusted after industrial production.
| Original Document | Technical Datasheet(English) | |||
| Features | High Stiffness/RigidityHeat ResistanceHeat StabilizedGood Heat AgingGood SurfaceEasy processingChemical ResistanceFilled & Reinforced | |||
| Additive | Heat Stabilizer | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Compliance | REACH (EC 1907/2006)RoHS | |||
| Reinforced | 50% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
Across Flow | *** % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | Dry. 1 mm/min |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | cond., 1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | Dry. |
Break | *** Mpa | ISO 527-1/-2 | cond. |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | Dry. |
Break | *** % | ISO 527-1/-2 | cond. |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | |
Melt Temperature(Tm) | *** °C | ISO 11357-1 | 10°C/min |
Continuous Use Temperature | |||
Long term | *** °C | Internal | 2000 hours |
Long term | *** °C | Internal | 3000 hours |
Processing Temperature | ***~*** °C | - | |
Mould temperature | ***~*** °C | - |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.