TECHNYL eXten® D 437P Natural is an unfilled polyamide 6.10, medium viscosity, unfilled, plasticized, UV and heat stabilized, for extrusion applications. This polyamide 6,10 for extrusion is specially performing where high flexibility and toughness are requested. It is specially developed for automotive and other applications where a long term high temperature usage is requested. It is a partially bio-sourced material.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好冲击性热稳定耐热老化含可再生资源抗紫外线耐化学性中粘度低吸湿性 | |||
| 添加助剂 | 紫外线稳定剂热稳定剂增塑剂 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 挤出 | |||
| 法规认证 | REACH (EC 1907/2006)RoHS(欧盟电子电气设备中有害物质) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.09 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 1.9 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
横向(Across Flow) | 1.9 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
吸水率 | 1.9 % | ISO 62 | |
吸水率 | 0.65 % | ISO 62 | 24 hr, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 44 Mpa | ISO 527-1/-2 | Dry |
断裂(brk) | 40 Mpa | ISO 527-1/-2 | cond. |
拉伸延伸率 | |||
断裂(brk) | 200 % | ISO 527-1/-2 | Dry |
断裂(brk) | 200 % | ISO 527-1/-2 | cond. |
弯曲模量 | 720 Mpa | ISO 178 | Dry. 2 mm/min |
弯曲模量 | 470 Mpa | ISO 178 | cond., 2 mm/min |
拉伸模量 | 820 Mpa | ISO 527-1/-2 | Dry. 1 mm/min |
拉伸模量 | 450 Mpa | ISO 527-1/-2 | cond., 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 3 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 14 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 140 kJ/m² | ISO 179/1eA | cond. |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 128 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 52 °C | ISO 75 | |
熔融温度(Tm) | 215 °C | ISO 11357-1 | 10°C/min |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。